Construction:
TEADIT style NA-1005 is a compressed non-asbestos
jointing-sheet material produced from Aramid-
and cellulose fibres, bonded with Nitrile rubber
(NBR). It is being manufactured by means of
a hot calender process under rigorous quality
control standards which are registered under
ISO 9001 certification.
Application / service:
Style NA-1005 is indicated for air, brine, water,
low pressure steam, organic and weak inorganic
acids, diluted and concentrated alkalis, petroleum
derivatives, synthetic and vegetable oils, aliphatic
and chlorinated solvents, refrigerants, gases
and chemical products in general.
Technical data:
Peak temperature:
+ 400°C
Constant temperature:
+ 240°C
Peak pressure:
up to 110 bar
Constant working pressure:
50 bar
Colour:
blue
Product standard:
thickness:
0,5 / 1,0 / 1,5 / 2,0 / 2,5 and 3,0 mm
sheet size:
1.500 x 1.600 mm, 1.500 x 3.200 mm
|
Typical physical properties
NA-1005 |
|
Test method |
Physical properties
|
Values |
|
ASTM F 36 |
Compressibility
|
7 - 17 % |
|
ASTM F 36 |
Recovery |
45 % |
|
ASTM F 146 |
Weight increase:
5h/ASTM oil / Nr.3
@ +150°C
5h/ASTM Fuel B
@ +21-29°C
|
15 %
15 % |
|
ASTM F 146 |
Thickness increase:
5h/ASTM oil / Nr.3
@ +150°C
ASTM Fuel B
@ +21-29°C |
12 %
10 % |
|
ASTM F 152 |
Tensile strength, transverse
|
11,5 N/mm²
|
|
DIN 52913 |
Residual stress
|
28 N/mm² |
|
ASTM F 38 |
Creep Relaxation |
25 % |
|
ASTM F 37 A |
Sealability at 1000 psi,
ml/h |
0,25 ml/h |
|
- |
Density |
app. 1,75 g/cm³
|